| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | 370 - 400 |
| Density | g mL-1 | 1.51 - 1.53 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 1.8 - 4.-5 |
| Heat Deflection Temperature, 0.5 MPa | °C | - |
| Heat Deflection Temperature, 1.8 MPa | °C | 330 - 380 |
| Thermal Conductivity | W / mK | 0.3 |
| Rockwell Hardness, M Scale | n/a | |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 180 - 200 |
| Tensile Strength, Break at 23 C | MPa | 115 - 130 |
| Elongation, Yield | % | |
| Elongation, Break | % | 2.3 - 2.8 |
| Tensile Modulus at 23 C | MPa | 11700 |
| Flexural Strength, Yield | MPa | 270 - 300 |
| Flexural Modulus | MPa | 11000 - 12000 |
| Compressive Strength | MPa | 250 - 290 |
| Izod Notched | kJ / m2 | 8.4 - 10.9 |
| Izod Unnotched | kJ / m2 | 40 - 69 |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | 2.5 - 3.1 | |
| Dielectric Constant @ 1 MHz | n/a | 3.3 | |
| Dissipation Factor @ 1 MHz | n/a |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 370 - 400 | |
| Mold Shrinkage | % | 0.3 - 0.9 | |
| Continuous Service Temperature | °C | 220 - 250 | |
| Water Absorption, 24 hr. Immersion | % |